Imec and Holst Centre unveil fully-organic imager

At this week’s International Image Sensor Workshop (IISW 2013, Snowbird, Utah, June 12-16 2013), imec and Holst Centre presented a large-area fully-organic photodetector array fabricated on a flexible substrate. The imager is sensitive in the wavelength range suitable for x-ray imaging applications.

Because of their very high absorption coefficient, organic semiconductors allow extremely thin active layers (10 to 50 nm). Also, given their low processing temperature, they can be processed on foils. As a result, organic imagers can be more robust and light-weight compared to their traditional counterparts and may be used for conformal coating of randomly shaped substrates. Moreover, the wide variety of organic molecules available ensures that the properties of the active layer can be tuned to applications requiring specific wavelength ranges.

The presented imager is sensitive in the wavelength range between 500 and 600nm, making it compatible with typical scintillators and therefore suitable for x-ray imaging applications. It was fabricated by thermally evaporating an ultrathin (submicron) photosensitive layer of small, organic molecules (SubPc/C60) on top of an organic readout circuit. A semi-transparent top contact enables front-side illumination. The readout backplane was manufactured on six-inch foil-laminated wafers. It consists of pentacene-based thin-film transistors (TFTs) in arrays of 32×32 pixels with varying pitch (1 mm and 200 µm). To prevent degradation of the organic semiconductors in the air, the photodetector array is encapsulated. The imager was characterized under illumination with a calibrated green light-emitting diode (LED), yielding a linearly increasing photocurrent from the incident power of 3 µW/cm2. Dark current density is below 10-6 A/cm2 at a bias voltage of -2V.

organic, flexible imager
Fully-organic, flexible imager developed by imec, Holst Centre and Philips Research

“This latest achievement is a significant step forward in not only finding the optimal materials, but pinpointing the best ways to process materials into reliable organic circuits and systems with state-of-the-art performance,” said Paul Heremans, technology director at the imec/Holst Centre. “Once again, we’re proud to demonstrate how imec’s top-notch research leads to relevant industrial solutions, and subsequently brings added value to our partners’ businesses.”

This research results are presented in collaboration with Philips Research, at the (2013 International Image Sensor Workshop (IISW), sponsored by the International Image Sensor Society (IISS), June 12-16, 2013.

POST A COMMENT

Easily post a comment below using your Linkedin, Twitter, Google or Facebook account. Comments won't automatically be posted to your social media accounts unless you select to share.

Leave a Reply

Your email address will not be published. Required fields are marked *

NEW PRODUCTS

KLA-Tencor announces new defect inspection systems
07/12/2018KLA-Tencor Corporation announced two new defect inspection products at SEMICON West this week, addressing two key challenges in tool and process monit...
3D-Micromac unveils laser-based high-volume sample preparation solution for semiconductor failure analysis
07/09/2018microPREP 2.0 provides order of magnitude time and cost savings compared to traditional sample...
Leak check semiconductor process chambers quickly and reliably
02/08/2018INFICON,a manufacturer of leak test equipment, introduced the UL3000 Fab leak detector for semiconductor manufacturing maintenance teams t...